PENGARUH PENAMBAHAN SILIKA 5% DARI PASIR LAUT TERHADAP PERUBAHAN DIMENSI GLASS IONOMER CEMENT SETELAH PERENDAMAN KOPI ARABIKA GAYO

BACA FULL TEXT ABSTRAK Pemesanan Versi cetak
Pengarang Halisni - Personal Name
SubjectORGANIC CHEMISTRY
SURVACTANTS
Bahasa Indonesia
Fakultas Fakultas Kedokteran Gigi Universitas Syiah Kuala
Tahun Terbit 2019

Abstrak/Catatan

ABSTRAK Nama : Halisni Program Studi : Pendidikan Dokter Gigi Fakultas : Kedokteran Gigi Judul : Pengaruh Penambahan Silika 5% dari Pasir Laut terhadap Perubahan Dimensi Glass Ionomer Cement (GIC) Setelah Perendaman Kopi Arabika Gayo Glass ionomer cement (GIC) adalah bahan restorasi yang paling sering digunakan karena merupakan material yang paling biokompatibel. Salah satu kandungan dari GIC adalah silika. Silika merupakan senyawa hasil polimerisasi dari asam silikat. Restorasi GIC apabila berada dalam keadaan lembab akan mengalami perubahan dimensi. Perubahan dimensi adalah perubahan yang terjadi pada material kedokteran gigi yang dapat disebabkan oleh penyerapan air. Tujuan: untuk mengetahui pengaruh penambahan 5% silika dari pasir laut terhadap perubahan dimensi glass ionomer cement (GIC) setelah perendaman kopi arabika gayo. Metode: jenis penelitian adalah eksperimental laboratoris. Spesimen penelitian berjumlah 8 spesimen yang berbentuk silinder. Spesimen dibagi menjadi 2 kelompok, yaitu 4 spesimen GIC konvensional dan 4 spesimen GIC dengan penambahan SiO2 kemudian kelompok tersebut diberikan perlakuan dengan perendaman kopi arabika gayo selama 4 hari di dalam inkubator dengan suhu 55oC. Setelah itu dilakukan pengukuran perubahan dimensi dengan menghitung berat spesimen dibagi luas permukaan. Hasil: data dianalisis menggunakan Statistical Package for the Social Sciences (SPSS) dengan uji mann whitney yang menunjukkan bahwa tidak terdapat perbedaan yang signifikan antara GIC konvensional dan GIC dengan penambahan silika (SiO2) setelah dilakukan perendaman dengan kopi arabika gayo (p>0,05). Kesimpulan: hasil penelitian ini menunjukkan bahwa rata-rata perubahan dimensi pada GIC dengan penambahan silika (SiO2) lebih besar daripada GIC konvensional, namun perubahan dimensi tersebut tidak signifikan. Kata Kunci: Glass ionomer cement (GIC), silika, perubahan dimensi   ABSTRACT Name : Halisni Study Program : Dentist Education Faculty : Dentistry Tittle : Effect of Addition of 5% Silica from Sea Sand to Dimensional Change of Glass Ionomer Cement (GIC) after Immersion of Gayo Arabica Coffee Glass ionomer cement (GIC) is the most commonly used restoration material because it is the most biocompatible material. One of the ingredients of GIC is silica. Silica is a compound resulting from polymerization of silicic acid. Restoration GIC when in a humid state will experience dimensinal changes. Dimensional changes are changes that occur in dental materials that can be caused by water absorption. Objective: To determine the effect of adding 5% silica from sea sand to dimensional change of glass ionomer cement (GIC) after immersion of gayo arabica coffee. Method: This type of research is an experimental laboratory. The total of specimens were 8 cylindrical specimens. Specimens were divided into 2 groups, which is 4 conventional GIC specimens and 4 GIC specimens with the addition of SiO2 then the group was immersed in gayo arabica coffee for 4 days in an incubator at 55oC temperature. Measurement of dimensional changes is by calculating the weight of the specimen divided by the surface area. Results: Data were analyzed using Statistical Package for Social Sciences (SPSS) with mann whitney that showed no significant difference between conventional GIC and GIC with the addition of SiO2 after immersion with gayo arabica coffee (p> 0.05) Conclusion: The results of this study indicate that the average dimensional change in GIC with the addition of silica (SiO2) is greater than conventional GIC, but the dimensional change is not significant. Keywords: Glass ionomer cement (GIC), silica, dimensional change

Tempat Terbit Banda Aceh
Literature Searching Service

Hard copy atau foto copy dari buku ini dapat diberikan dengan syarat ketentuan berlaku, jika berminat, silahkan hubungi via telegram (Chat Services LSS)

Share Social Media

Tulisan yang Relevan

GAMBARAN MIKROSTRUKTUR PERMUKAAN GIC KOVENSIONAL DAN DENGAN PENAMBAHAN KITOSAN 10 V/V % SETELAH PERENDAMAN DALAM KOPI ARABIKA GAYO (TANTI JERNITA, 2016)

PENGARUH PENAMBAHAN SILIKA DARI PASIR PANTAI TERHADAP PERUBAHAN WARNA GLASS IONOMER CEMENT (GIC) SETELAH PERENDAMAN KOPI ARABIKA GAYO (RABITHAH NASUTION, 2019)

KEKASARAN PERMUKAAN GLASS IONOMER CEMENT (GIC) TANPA DAN DENGAN PENAMBAHAN KITOSAN SETELAH PERENDAMAN DALAM KOPI ARABIKA GAYO (Dewi Setianingrum, 2015)

PENGARUH PENAMBAHAN HIDROKSIAPATIT PADA POWDER GLASS IONOMER CEMENT TERHADAP PERUBAHAN WARNA SETELAH PERENDAMAN DA0LAM KOPI ARABIKA GAYO (NAURAH NAZHIFAH, 2019)

KEKERASAN PERMUKAAN GLASS IONOMER CEMENT (GIC) SETELAH PENAMBAHAN 5% SILIKA DARI PASIR LAUT (Apriliadi Saputra, 2018)