SINTESIS FOTOKATALIS KOMPOSIT TIO DARI BIJIH BESI DENGAN METODE SONIKASI DAN APLIKASINYA PADA FOTODEGRADASI ZAT WARNA INDIGO KARMIN

BACA FULL TEXT ABSTRAK Pemesanan Versi cetak
Pengarang KHALIDINUL IHSAN - Personal Name
SubjectCATALYSIS - ORGANIC CHEMISTRY
IRON - MATERIAL SCIENCE
Bahasa Indonesia
Fakultas FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM UNIVERSITAS SYIAH KUALA
Tahun Terbit 2019

Abstrak/Catatan

Modifikasi hematit (α-Fe 2 O 3 ABSTRAK ) dengan TiO untuk menghasilkan komposit TiO 2 /α-Fe 2 O 3 2 melalui metode sonikasi serta uji aktivitas fotokatalitiknya pada degradasi zat warna indigo karmin telah dilakukan. Hematit diestraksi dari bijih besi menggunakan asam klorida (HCl) dan presipitasi menggunakan ammonium hidroksida (NH OH). Titanium (IV) dioksida yang digunakan berasal dari titanium tetraisopropoksida. Fotokatalis komposit TiO 4 2 /α-Fe dipreparasi dengan perbandingan mol TiO 2 dan α-Fe 2 O 3 2 1:3, 3:1 dan 1:1. Karakterisasi menggunakan X-Ray Diffraction (XRD) dan Scanning Electron MicroscopyEnergy Dispersive X-Ray Spectroscopy (SEM-EDS) dilakukan untuk mengetahui sifat fisik dan kimia dari hematit dan komposit TiO 2 /α-Fe 2 O . Hasil uji aktivitas fotokatalitik menunjukkan bahwa fotokatalis komposit TiO 3 2 O 3 /α-Fe dengan perbandingan mol TiO 2 dan α-Fe 2 O 1:3 memiliki aktivitas paling tinggi, dengan persen degradasi (% D) sebesar 92,70% menggunakan sinar ultra violet; 90,99% menggunakan lampu flouresen dan 94,06% menggunakan sinar matahari. Aktivitas fotokatalitik tersebut diperoleh pada kondisi pH larutan zat warna = 1, massa fotokatalis 350 mg, konsentrasi awal zat warna 20 ppm, dengan waktu radiasi 120 menit menggunakan sinar UV dan lampu flouresen serta 30 menit menggunakan cahaya matahari. Kata kunci : Fotokatalis, Indigo karmin, α-Fe Modification of hematite (α-Fe 3 2 ABSTRACT 2 O 3 O 3 dan TiO ) with TiO 2 2 /α-Fe 2 O 3 to produce TiO composites by sonication method and their photocatalytic activity testing on the degradation of indigo carmine dyes has been done. The hematite was etracted from iron sand by using hydrochloric acid (HCl) and precipitation by using ammonium hydroxide (NH OH). The precursor of titanium (IV) dioxide was titanium tetraisopropoxide. TiO 4 2 /α-Fe 2 O composites photocatalysts were prepared with the mole ratio of TiO 2 to α-Fe 3 2 O 1;3, 3;1 and 1;1. Characterization of α-Fe 2 O 3 and TiO 2 /α-Fe 2 O 3 3 composites was carried out in order to determine their physical and chemical properties. The result photocatalytic activities testing showed that the TiO 2 /α-Fe 2 O 3 composite with the mole ratio of TiO 1;3 has the highest activity with the percent degradation (%D) of indigo carmine dye was 92.70 % under ultra violet light ; 90.99 % under fluorescent lamp and 94.06 % under solar light irradiation, respectively. These highest photocatalytic activity were obtained at the initial pH of dye solution 1, the photocatalyst mass of 350 mg, the initial dye concentration was 20 ppm, irradiation time 120 minutes under UV light and fluorescent lamp and 30 minutes under solar light irradiation. Keywords : photocatalyst, indigo carmine, α-Fe 2 O 3 and TiO 2 /α-Fe 2 O 2 2 3 O 3 2 /α-Fe to α-Fe 2 2 O O 3 3

Tempat Terbit Banda Aceh
Literature Searching Service

Hard copy atau foto copy dari buku ini dapat diberikan dengan syarat ketentuan berlaku, jika berminat, silahkan hubungi via telegram (Chat Services LSS)

Share Social Media

Tulisan yang Relevan

PEMANFAATAN PASIR BESI PADA SINTESIS FOTOKATALIS FE2O3/TIO2 DAN UJI AKTIFITASNYA PADA DEGRADASI ZAT WARNA INDIGO KARMIN (Masyithah, 2017)

PEMBUATAN FOTOKATALIS KOMPOSIT ZNO/α-FE2O3 DENGAN METODE IMPREGNASI-SONIKASI DAN UJI AKTIVITAS FOTOKATALITIKNYA PADA DEGRADASI ZAT WARNA INDIGO CARMINE (Nesti, 2018)

PEMANFAATAN BIJIH BESI PADA SINTESIS FOTOKATALIS α-FE2O3/TIO2 DAN UJI AKTIVITASNYA PADA DEGRADASI ZAT WARNA INDIGO KARMIN (Ibnu Hajar Al-Haitami, 2017)

PEMANFAATAN PASIR BESI PADA SINTESIS FOTOKATALIS ZNO/α-FE2O3 DAN UJI AKTIVITAS FOTOKATALITIKNYA PADA DEGRADASI ZAT WARNA INDIGO KARMIN (Octavia Ningsih, 2019)

PEMANFAATAN PASIR BESI PADA SINTESIS FOTOKATALIS FE2O3/TIO2 DAN UJI AKTIVITASNYA PADA DEGRADASI ZAT WARNA INDIGO KARMIN (Masyithah, 2017)

  Kembali ke sebelumnya

Pencarian

Advance



Jenis Akses


Tahun Terbit

   

Program Studi

   

© UPT. Perpustakaan Universitas Syiah Kuala 2015     |     Privacy Policy