FOTODEGRADASI ZAT WARNA INDIGO CARMINE MENGGUNAKAN FOTOKATALIS α-FE2O3/BENTONIT

BACA FULL TEXT ABSTRAK Pemesanan Versi cetak
Pengarang AFRI ALZAHRA - Personal Name
SubjectCATALYSIS - ORGANIC CHEMISTRY
IRON - MATERIAL SCIENCE
Bahasa Indonesia
Fakultas FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM UNIVERSITAS SYIAH KUALA
Tahun Terbit 2018

Abstrak/Catatan

ABSTRAK Penelitian mengenai fotodegradasi zat warna indigo carmine (IC) menggunakan fotokatalis komposit α-Fe2O3/bentonit dan radiasi sinar ultraviolet (UV) telah dilakukan. Hematit (α-Fe2O3) disintesis dari pasir besi yang berasal dari pantai Syiah Kuala, Banda Aceh melalui metode kopresipitasi. Fotokatalis komposit α-Fe2O3/bentonit dipreparasi dengan menggunakan metode ball mill dengan variasi perbandingan berat (b/b) α-Fe2O3 dan bentonit 3:1, 1:3 dan 1:1. Hematit dan fotokatalis komposit α-Fe2O3/bentonit dikarakterisasi menggunakan (X-Ray Diffraction) (XRD) dan (Scanning Electron Microscopy-Energy Dispersive X-Ray) (SEM EDX) untuk mengetahui sifat fisik dan kimianya. Berdasarkan hasil analisis XRD oksida besi yang diperoleh memiliki fasa α-Fe2O3 dan rata-rata ukuran kristal fotokatalis komposit α-Fe2O3/bentonit lebih kecil dibandingkan dengan hematit dan bentonit. Aktivitas fotokatalitik komposit α-Fe2O3/bentonit yang tertinggi diperoleh pada perbandingan α-Fe2O3 dan bentonit 3:1 dengan persen degradasi IC sebesar 89% pada kondisi pH larutan zat warna 1, massa fotokatalis 350 mg, dan konsentrasi zat warna 15 ppm setelah diradiasi dengan sinar UV selama 120 menit. Fotokatalis komposit α-Fe2O3/bentonit menggunakan cahaya matahari menunjukkan aktivitas yang lebih tinggi dibanding menggunakan sinar UV dengan persen degradasi zat warna IC mencapai 93%. Kata Kunci: Fotokatalis, Indigo Carmine, α-Fe2O3 dan bentonit. ABSTRACT Research on photodegradation of indigo carmine (IC) dye using α-Fe2O3/bentonite composite photocatalyst and ultraviolet (UV) irradiation has been conduction. Hematite (α-Fe2O3) was synthesized from iron sand from Syiah Kuala beach, Banda Aceh through coprecipitation methods. α-Fe2O3/bentonite composite photocatalysts were prepared using ball mill method with various weight ratio (w/w) α-Fe2O3 and bentonite 3:1, 3:1 and 1:1. Hematite and α-Fe2O3/bentonite composite photocatalysts are characterized by using X-Ray Diffraction (XRD) and Scanning Electron Microscopy-Energy Dispersive X-Ray (SEM EDX) in order to determine their physical and chemical properties. Based on the results of XRD, iron oxide obtained has a α-Fe2O3 phase and the average crystallite size of the composite are smaller than that of hematite and bentonite. The highest photocatalytic activity of α-Fe2O3/bentonite composite was obtained at a weight ratio α-Fe2O3 and bentonite was 3:1 with the IC degradation of 89% at the initial pH of dye solution was 1, 350 mg photocatalyst mass, and 15 ppm of initial dye concentration after being irradiated with UV light for 120 minutes. The photocatalytic activity of α-Fe2O3/bentonite composite photocatalyst under sunlight irradiation is higher than that of under UV irradiation Keyword: Photocatalytic, Indigo Carmine, α-Fe2O3 and bentonite

Tempat Terbit Banda Aceh
Literature Searching Service

Hard copy atau foto copy dari buku ini dapat diberikan dengan syarat ketentuan berlaku, jika berminat, silahkan hubungi via telegram (Chat Services LSS)

Share Social Media

Tulisan yang Relevan

FOTODEGRADASI ZAT WARNA INDIGO CARMINE MENGGUNAKAN KOMPOSIT α-FE2O3 DARI BIJIH BESI/BENTONIT (Murisna, 2017)

DEGRADASI ZAT WARNA KATIONIK DAN ANIONIK MENGGUNAKAN IMMOBILISASI FOTOKATALIS TIO2/α-FE2O3/BENTONIT DIBAWAH LAMPU FLUORESCENCE (FERIZKA FRASTIWI, 2018)

PEMBUATAN FOTOKATALIS KOMPOSIT ZNO/α-FE2O3 DENGAN METODE IMPREGNASI-SONIKASI DAN UJI AKTIVITAS FOTOKATALITIKNYA PADA DEGRADASI ZAT WARNA INDIGO CARMINE (Nesti, 2018)

PREPARASI KOMPOSIT TIO2-BENTONIT DAN TIO2-KRISTOBALIT DAN SERTA APLIKASINYA PADA FOTODEGRADASI INDIGO CARMINE (Ulfa Rianda, 2018)

PILARISASI BENTONIT TERAKTIVASI MENGGUNAKAN TIO2 DAN APLIKASINYA PADA DEGRADASI ZAT WARNA (Syahrinta Sepia Nika, 2016)

  Kembali ke sebelumnya

Pencarian

Advance



Jenis Akses


Tahun Terbit

   

Program Studi

   

© UPT. Perpustakaan Universitas Syiah Kuala 2015     |     Privacy Policy