KEKERASAN PERMUKAAN GLASS IONOMER CEMENT (GIC) SETELAH PENAMBAHAN 5% SILIKA DARI PASIR LAUT

BACA FULL TEXT ABSTRAK Pemesanan Versi cetak
Pengarang Apriliadi Saputra - Personal Name
SubjectDENTAL RESTORATION (GLASS IONOMER CEMENT) GIC
Bahasa Indonesia
Fakultas Fakultas Kedokteran Gigi Universitas Syiah Kuala
Tahun Terbit 2018

Abstrak/Catatan

ABSTRAK Nama : Apriliadi Saputra Fakultas : Kedokteran Gigi Program Studi : Pendidikan Dokter Gigi Judul : Kekerasan Permukaan Kekerasan Permukaan Glass Ionomer Cement (GIC) Setelah Penanambahan 5% Silika Dari Pasir Laut Glass ionomer cement (GIC) adalah semen berbasis air, yang telah banyak digunakan sebagai bahan restorasi gigi yang terdiri atas bubuk flouroaluminosilikat dan larutan asam poliakrilat. GIC memiliki kelemahan sebagai bahan restorasi yaitu tidak bisa digunakan untuk merestorasi gigi dengan beban kunyah yang besar. Penambahan silika dalam GIC menjadi salah satu aspek yang perlu dipertimbangkan karena silika mempunyai sifat kekerasan yang tinggi. Sumber silika dapat disintesis dari pasir laut dimana memiliki kandungan silika sekitar 98%. Penelitian ini bertujuan untuk mengetahui perbedaan kekerasan permukaan dari GIC konvensional dan GIC dengan penambahan 5% silika dari pasir laut. Spesimen dibuat berbentuk silinder dengan ukuran diameter 5 mm dan tinggi 2 mm, berjumlah 10 spesimen yaitu 5 spesimen GIC konvensional tipe II (kelompok kontrol) dan 5 spesimen GIC konvensional dengan penambahan silika dari pasir laut (kelompok perlakuan ). Vickers Hardness Tester digunakan untuk pengukuran nilai kekerasan. Data dianalisis menggunakan SPSS dengan uji t tidak berpasangan. Hasil data menunjukkan bahwa tidak ada perbedaan yang nyata (p>0.05) antara kekerasan permukaan GIC konvensional dan GIC dengan penambahan silika dari pasir laut. Kata Kunci: Glass Ionomer Cement, Silika, Kekerasan Permukaan ABSTRACT Name : Apriliadi Saputra Faculty : Dentistry Study Program : Dentist Title : Surface Hardness of Glass Ionomer Cement (GIC) After Addition of 5% Silica from Sea Sand Glass ionomer cement (GIC) is a water-based cement, which has been widely used as a dental restoration material consisting of flouroaluminosilicate powder and polyacrylic acid solution. GIC has a weakness as a restoration material that cannot be used to restore teeth with a large chewing load. The addition of silica in GIC is one aspect that needs to be considered because silica has a high hardness. The source of silica can be synthesized from sea sand which has a silica content of around 98%. This study aims to determine the differences in surface hardness of glass ionomer cement (GIC) and GIC with the addition of 5% silica from sea sand. Specimens were made in a cylindrical shape with a diameter of 5 mm and a height of 2 mm, totaling 10 specimens, namely 5 conventional type II GIC specimens (control group) and 5 conventional GIC specimens with the addition of silica from sea sand (treatment group). Vickers Hardness Tester is used to measure the value of hardness. Data analyzed using SPSS with unpaired t test showed that there was no significant difference (p> 0.05) between the surface hardness of glass ionomer cement and GIC with the addition of silica from sea sand. Keyword: Glass Ionomer Cement, Silica, Surface Hardness

Tempat Terbit Banda Aceh
Literature Searching Service

Hard copy atau foto copy dari buku ini dapat diberikan dengan syarat ketentuan berlaku, jika berminat, silahkan hubungi via telegram (Chat Services LSS)

Share Social Media

Tulisan yang Relevan

GAMBARAN PERLEKATAN GLASS IONOMER CEMENT MODIFIKASI SILIKA 5% DARI PASIR LAUT DENGAN GIGI MENGGUNAKAN SCANNING ELECTRON MICROSCOPE (SEM) (DWI SEPTIANI, 2019)

ANALISIS HASIL MODIFIKASI GLASS IONOMER CEMENT DENGAN PENAMBAHAN HIDROKSIAPATIT DAN SILIKA DARI BAHAN ALAM (DITINJAU DARI GUGUS FUNGSI MENGGUNAKAN FOURIER TRANSFORM INFRARED) (MOHD TAUFIQ KAMIL H, 2018)

PENGARUH PENAMBAHAN SILIKA 5% DARI PASIR LAUT TERHADAP PERUBAHAN DIMENSI GLASS IONOMER CEMENT SETELAH PERENDAMAN KOPI ARABIKA GAYO (Halisni, 2019)

GAMBARAN PENGGUNAAN BAHAN AMALGAM, RESIN KOMPOSIT DAN GLASS IONOMER CEMENT (GIC) DI RUMAH SAKIT GIGI DAN MULUT UNSYIAH PADA BULAN JULI – DESEMBER 2014 (Nur Shabrina, 2016)

KEKERASAN PERMUKAAN GLASS IONOMER CEMENT SETELAH PENAMBAHAN 5% HIDROKSIAPATIT DARI CANGKANG KERANG DARAH (ANADARA GRANOSA) (FIKRIYADI NURZAL, 2018)

  Kembali ke sebelumnya

Pencarian

Advance



Jenis Akses


Tahun Terbit

   

Program Studi

   

© UPT. Perpustakaan Universitas Syiah Kuala 2015     |     Privacy Policy