ADSORPSI LOGAM KADMIUM (CD) MENGGUNAKAN MONTMORILLONIT TERMODIFIKASI KARBON AKTIF CANGKANG KELAPA SAWIT | ELECTRONIC THESES AND DISSERTATION

Electronic Theses and Dissertation

Universitas Syiah Kuala

    SKRIPSI

ADSORPSI LOGAM KADMIUM (CD) MENGGUNAKAN MONTMORILLONIT TERMODIFIKASI KARBON AKTIF CANGKANG KELAPA SAWIT


Pengarang

Sulastri - Personal Name;

Dosen Pembimbing

Julinawati - 197107011997022001 - Dosen Pembimbing I
Irfan Mustafa - 197411302002121001 - Dosen Pembimbing II



Nomor Pokok Mahasiswa

1708103010004

Fakultas & Prodi

Fakultas MIPA / Kimia (S1) / PDDIKTI : 47201

Subject
-
Kata Kunci
-
Penerbit

Banda Aceh : Fakultas MIPA - Kimia., 2022

Bahasa

No Classification

-

Literature Searching Service

Hard copy atau foto copy dari buku ini dapat diberikan dengan syarat ketentuan berlaku, jika berminat, silahkan hubungi via telegram (Chat Services LSS)

Telah dilakukan penelitian tentang adsorpsi logam kadmium (Cd) menggunakan montmorillonit (MMT) termodifikasi karbon aktif cangkang kelapa sawit. Penelitian ini terdiri dari beberapa tahap yaitu mengisolasi bentonit alam menjadi MMT, pembuatan karbon aktif dari cangkang kelapa sawit dan memodifikasi MMT dengan karbon aktif. Adsorben dikarakterisasi menggunakan Fourier Transform Infrared (FTIR), X-Ray Diffraction (XRD), dan Scanning Electron Microscope (SEM) serta diuji daya serapnya terhadap logam kadmium (Cd) dengan menggunakan instrumen Spektrofotometri UV-Vis. Penentuan kondisi optimum pada proses adsorpsi dilakukan dengan variasi massa adsorben, variasi waktu kontak, variasi pH, dan variasi konsentrasi dari ion logam kadmium (Cd) dengan kecepatan pengadukan 200 rpm. MMT telah dapat termodifikasi dengan karbon aktif cangkang kelapa sawit yang dibuktikan pada FTIR dengan bergesernya beberapa bilangan gelombang dan adanya perubahan intensitas pita serapan baru yaitu pada bilangan gelombang 2200,87 cm-1 yang menunjukkan gugus fungsi C≡C. Hasil XRD menunjukkan telah terjadi penurunan intensitas sudut 2θ jika dibandingkan dengan MMT sebelum modifikasi. Hasil SEM menunjukkan bahwa partikel yang dihasilkan setelah proses modifikasi memiliki partikel dengan tekstur relatif lebih halus dan memiliki bentuk morfologi yang lebih rapat serta memiliki ukuran pori yang seragam dan terdistribusi merata. Kondisi adsorpsi optimum logam Cd menggunakan MMT termodifikasi karbon aktif cangkang kelapa sawit terjadi pada massa 0,1 g dan waktu kontak 75 menit serta pH 9 dengan efisiensi penyerapan sebesar 91,01% dan kapasitas adsorpsi yaitu 3,4130 mg/g. Persamaan isoterm adsorpsi yang sesuai untuk menggambarkan proses adsorpsi logam Cd adalah mengikuti persamaan isoterm adsorpsi Freundlich dengan nilai R2 sebesar 0,9811.

Kata kunci: Montmorillonit, cangkang kelapa sawit, karbon aktif, efisiensi penyerapan, kapasitas adsorpsi, isoterm adsorpsi, kadmium (Cd)

Research on the adsorption of metal cadmium (Cd) has been carried out using montmorillonite (MMT) modified with palm kernel shell activated carbon. This research consisted of several stages, namely isolating natural bentonite into MMT, making activated carbon from oil palm shells and modifying montmorillonite with activated carbon. The adsorbents were characterized using Fourier Transform Infrared (FTIR), X-Ray Diffraction (XRD), and Scanning Electron Microscope (SEM) and tested for their absorption capacity against metal cadmium (Cd) using a UV-Vis spectrophotometric instrument. Determination of the optimum conditions for the adsorption process was carried out by varying the mass of the adsorbent, variations in contact time, variations in pH, and variations in the concentration of cadmium metal ions (Cd) with a stirring speed of 200 rpm. MMT has been able to be modified with activated carbon from oil palm shells as evidenced in FTIR by shifting some wave numbers and a change in the intensity of the new absorption band, namely at wave number of 2200,87 cm-1 which indicated the C≡C functional group. XRD results show that there has been a decrease in the intensity of the angle 2θ decreased, which means it was more amorphous when compared to MMT before being modified. SEM results show that the particles produced after the modification process have particles with relatively finer textures and have a denser morphology and has uniform and evenly distributed pore size. Optimum adsorption conditions for Cd metal using MMT modified palm shell activated carbon occurred at a mass of 0,1 g and a contact time of 75 minutes and pH 9 with an adsorption efficiency of 91,01% and an adsorption capacity of 3,4130 mg/g. The appropriate adsorption isotherm equation to describe the Cd metal adsorption process is as follows the Freundlich adsorption isotherm equation with an R2 value of 0,9811. Keywords: Montmorillonite, palm shell, activated carbon, absorption efficiency, adsorption capacity, adsorption isotherm, cadmium (Cd)