Octavia Ningsih. PEMANFAATAN PASIR BESI PADA SINTESIS FOTOKATALIS ZNO/?-FE2O3 DAN UJI AKTIVITAS FOTOKATALITIKNYA PADA DEGRADASI ZAT WARNA INDIGO KARMIN. Banda Aceh : Universitas Syiah Kuala, 2019

Abstrak

Abstrak sintesis fotokatalis komposit zno/?-fe2o3 yang dilakukan melalui metode ball mill dan uji aktivitas fotokatalitiknya pada degradasi zat warna indigo karmin telah dilakukan. hematit diekstraksi dari pasir besi yang berasal dari pantai syiah kuala, banda aceh dengan menggunakan asam klorida (hcl) dan presipitasi menggunakan ammonium hidroksida (nh4oh) pada ph 6. komposit zno/?fe2o3 dipreparasi dengan perbandingan mol zno:?-fe2o3 1:1, 1:5 dan 5:1. karakterisasi dilakukan menggunakan scanning electron microscopy-energi dispersive x-ray spectroscopy (sem-edx) dan x-ray diffraction (xrd) untuk mengetahui sifat fisik dan kimia komposit zno/?-fe2o3. uji aktivitas fotokatalitik menunjukkan bahwa komposit zno/?-fe2o3 dengan perbandingan mol 1:5 memiliki aktivitas paling tinggi dengan persen degradasi (%d) sebesar 89,16% menggunakan sinar uv dan 91,96% menggunakan sinar matahari. kondisi reaksi yang memberikan persen degradasi tertinggi adalah pada ph larutan 1, massa fotokatalis 250

Baca Juga : PEMANFAATAN PASIR BESI PADA SINTESIS FOTOKATALIS FE2O3/TIO2 DAN UJI AKTIFITASNYA PADA DEGRADASI ZAT WARNA INDIGO KARMIN (Masyithah, 2017) ,

Baca Juga : PEMBUATAN FOTOKATALIS KOMPOSIT ZNO/?-FE2O3 DENGAN METODE IMPREGNASI-SONIKASI DAN UJI AKTIVITAS FOTOKATALITIKNYA PADA DEGRADASI ZAT WARNA INDIGO CARMINE (Nesti, 2018) ,

, konsentrasi larutan zat warna 15 ppm dengan waktu radiasi dengan sinar uv selama 120 menit dan sinar matahari selama 90 menit. kata kunci : fotokatalis, pasir besi, zno/?-fe2o3, ball mill dan indigo karmin abstract synthesis of zno/?-fe2o3 composite photocatalyst prepared by ball milling method and its photocatalytic activity on the degradation of indigo carmine dye has been carried out. hematite was extracted from iron sand taken from the coast of syiah kuala, banda aceh using hydrochloric acid (hcl) and precipitation using ammonium hydroxide (nh4oh) at ph 6. zno/?-fe2o3 composites are prepared on molar ratio of zno to ?-fe2o3 1:1, 1:5 and 5:1. characterization of materials were carried out using scanning electron microscopy-energi dispersive x-ray spectroscopy (sem-edx) and x-ray diffraction (xrd) to determine their physical and chemical properties of zno/?-fe2o3 composites. the photocatalytic activity of composite with the molar ratio of zno to ?-fe2o3 1:5 showed highest activity with percent of degradation (%d) of indigo carmine was 89,16% under uv light and 91,96% under solar light. condition of reaction with the highest photocatalytic activity was initial ph of solution 1, photocatalyst mass of 250 mg, concentration of dye solution 15 ppm with the irradiation time with uv light for 120 minutes and solar light for 90 minutes. keywords : photocatalyst, iron sand, zno/?-fe2o3, ball mill and indigo

Tulisan yang relevan

FOTODEGRADASI ZAT WARNA INDIGO CARMINE MENGGUNAKAN FOTOKATALIS ZNO/?-FE2O3 YANG DISINTESIS DENGAN METODE SOL-GEL (Linda Mahyuni, 2018) ,

PEMANFAATAN PASIR BESI PADA SINTESIS FOTOKATALIS ZNO/?-FE2O3 DAN UJI AKTIVITAS FOTOKATALITIKNYA PADA DEGRADASI ZAT WARNA INDIGO KARMIN (Octavia Ningsih, 2019) ,

PEMBUATAN FOTOKATALIS ?-FE2O3/TIO2 DARI PASIR BESI DAN UJI AKTIVITAS FOTOKATALITIKNYA PADA PENGHILANGAN ZAT WARNA INDIGO KARMIN (Khairunnas Ahmad, 2019) ,


Kembali ke halaman sebelumnya


Pencarian

Advance



Jenis Akses


Tahun Terbit

   

Program Studi