PEMBUATAN KATALIS CUO MENGGUNAKAN METODE ELEKTRODEPOSISI DENGAN VARIASI H3BO3

BACA FULL TEXT ABSTRAK Pemesanan Versi cetak
Pengarang Ade Agus Hidayat - Personal Name

Abstrak/Catatan

ABSTRAK Telah dilakukan penelitian tentang pengaruh variasi asam boraks (H3BO3) pada sintesis katalis CuO melalui metode elektrodeposisi. Hasil karakterisasi XRD terhadap katalis A, C dan E menunjukkan ketiga katalis memiliki puncak serapan dominan CuO berfase tenorite dengan nilai d(A) masing-masing sebesar 2,52, 2,45 dan 2,46. Hasil penentuan ukuran partikel dengan menggunakan persamaan Debye-Scherrer pada ketiga katalis diperoleh informasi bahwa ukuran kristalin CuO pada katalis A, C dan E masing-masing sebesar 7,09 nm, 4,75 nm dan 5,72 nm. Penentuan morfologi terhadap CuO yang dihasilkan menggunakan SEM menunjukkan ketiga katalis berupa bongkahan dengan katalis A memiliki ukuran partikel katalis terkecil ±80 μm, sedangkan katalis E memiliki ukuran partikel katalis terbesar ±100 μm. Hasil penelitian menunjukkan bahwa katalis CuO dengan rasio mol CuSO4 dan H3BO3 sebesar 1 : 0,5 (katalis C) memiliki aktifitas katalis tertinggi dengan kemampuan degradasi pewarna metil biru sebesar 67,62% dan katalis CuO yang dihasilkan rasio mol CuSO4 dan H3BO3 sebesar 1 : 1 (katalis E) memiliki aktifitas katalis terendah dengan kemampuan degradasi pewarna metil biru sebesar 54,39%, sedangkan katalis CuO yang tanpa penambahan H3BO3 (katalis A) memiliki kemampuan degradasi pewarna metil biru sebesar 65,21%. Kata Kunci : Katalis CuO, Elektrodeposisi, Fotokatalitik, H3BO3. ABSTRACT The study on the effect variations of H3BO3 on CuO Synthesized using electrodeposition methods has been carried out succesfully. The results of physical characterization using XRD on the resulted CuO catalysts (A,C and E) shown that three catalysts have been a dominant absorption peaks as a CuO phased tenorite which the d(A) value are 2.52, 2.45 and 2.46, respectively. Particle size estimation by using the Debye-Scherrer equation on Synthesized CuO catalysts indicated that the particle size of A, C and E are 7.09 nm, 4,75 nm and 5.72 nm, respectively. Morphology characterization with employing SEM equipment shown that all catalysts have been taken agglomeration process, where as the CuO catalyst reffered as A has been the smallest particle size of 80 μm, approximately and the biggest size of particle found on CuO catalyst refered as E with its particle size is 100 μm approximately. Finally, Synthesized CuO indicated its catalytic activity on degradation of methylen blue dye. The results showed that the CuO catalyst with CuSO4 and H3BO3 mole ratio of 1: 0.5 (reffered as C ) has been the highest catalytic activity with degradation percentage of 67.62%, whereas the CuO catalyst prepared with mol rasio of CuSO4 : H3BO3 of 1: 1 ( referred as E) shown the lowest catalytic activity of 54.39%, however in case of CuO catalyst without dropping of H3BO3 in the sintisyzed proccess (reffered to A) shown its degradation ability is 65.21%. Keywords : CuO Catalyst, Electrodeposition, Photocatalytic, H3BO3.

Tempat Terbit
Literature Searching Service

Hard copy atau foto copy dapat diberikan dengan syarat ketentuan berlaku, jika berminat, silahkan isi formulir online (Formulir Online)

Share Social Media

Tulisan yang Relevan

DEGRADASI METHYLENE BLUE DENGAN METODE FOTOKATALISIS MENGGUNAKAN KATALIS LA-DOPED NATAO3 (Yusri Nadya, 2014)

¬PENGARUH SISIPAN KATALIS SIO2 DALAM MGH2 TERHADAP TEMPERATUR DESORPSI UNTUK APLIKASI MATERIAL PENYIMPAN HIDROGEN (ELISA PAJRIANA, 2015)

PREPARASI KATALIS HETEROGEN DARI LIMBAH TULANG SAPI ACEH DAN UJI AKTIVITASNYA PADA SINTESIS BIODIESEL (Rara Mitaphonna, 2018)

KONFERSI MINYAK JELANTAH MENJADI BIODIESEL MENGGUNAKAN KATALIS KALSIUM OKSIDA (CAO) DARI CANGKANG TELUR (Nova Mauliza, 2017)

PREPARASI KATALIS HETEROGEN ANORGANIK DARI LIMBAH TULANG IKAN CAKALANG (KATSUWONUS PELAMIS) DAN UJI AKTIVITAS KATALITIKNYA PADA SINTESIS BIODIESEL DARI MINYAK KELAPA (Desi Novita, 2018)

  Kembali ke sebelumnya

Pencarian

Advance



Jenis Akses


Tahun Terbit

   

Program Studi

   

© UPT. Perpustakaan Universitas Syiah Kuala 2015     |     Privacy Policy