DWI SEPTIANI. GAMBARAN PERLEKATAN GLASS IONOMER CEMENT MODIFIKASI SILIKA 5% DARI PASIR LAUT DENGAN GIGI MENGGUNAKAN SCANNING ELECTRON MICROSCOPE (SEM). Banda Aceh : Universitas Syiah Kuala, 2019

Abstrak

Abstrak nama : dwi septiani program studi : pendidikan dokter gigi fakultas : kedokteran gigi judul : gambaran perlekatan glass ionomer cement modifikasi silika 5% dari pasir laut dengan gigi menggunakan scanning electron microscope (sem) glass ionomer cement (gic) merupakan bahan restorasi yang paling biokompatibel. material gic merupakan bahan restorasi yang dapat melekat pada email dan dentin secara fisiko kimiawi. sifat adhesi gigi terhadap restorasi berpengaruh pada adaptasi marginal. hal ini menyebabkan perbedaan nilai perlekatan. perbedaan perlekatan tersebut dibutuhkan alternatif dengan menambahkan bahan bioactive glass silica pada powder gic. penelitian ini bertujuan untuk mendapatkan informasi tentang gambaran perlekatan glass ionomer cement modifikasi silika 5% dari pasir laut dengan gigi menggunakan scanning electron microscope. pada penelitian ini, silika disintesis dari pasir laut menggunakan metode kopresitipasi. spesimen penelitian berjumlah 4 gigi premolar

Baca Juga : ANALISIS HASIL MODIFIKASI GLASS IONOMER CEMENT DENGAN PENAMBAHAN HIDROKSIAPATIT DAN SILIKA DARI BAHAN ALAM (DITINJAU DARI GUGUS FUNGSI MENGGUNAKAN FOURIER TRANSFORM INFRARED) (MOHD TAUFIQ KAMIL H, 2018) ,

Baca Juga : KEKERASAN PERMUKAAN GLASS IONOMER CEMENT (GIC) SETELAH PENAMBAHAN 5% SILIKA DARI PASIR LAUT (Apriliadi Saputra, 2018) ,

ang atas dengan kavitas klas i kemudian direstorasi, lalu dibagi menjadi dua kelompok. kelompok a diaplikasikan gic (fuji ix) (n=2) dan kelompok b diaplikasikan dengan gic modifikasi silika 5% dari pasir laut (n=2). seluruh spesimen direndam dalam larutan pewarna biru 5% selama 24 jam kemudian dilakukan pengamatan dengan menggunakan scanning electron microscope (sem) dan diukur rerata jarak antara bahan restorasi dengan gigi (email dan dentin). hasil analisa deskriptif menunjukkan bahwa terdapat jarak antara bahan restorasi dengan permukaan gigi di bawah gambaran sem, dengan rerata jarak antara gic (fuji ix) dan permukaan email dan dentin yaitu sebesar 11.74 4.642 m dan 13.52 7.891 m sementara jarak antara gic modifikasi silika 5% dengan email dan dentin yaitu sebesar 6.31 1.086 m dan 9.33 2.361 m. kesimpulan penelitian ini adalah terdapat perbedaan nilai rerata jarak antara bahan restorasi gic modifikasi silika 5% dengan gigi lebih kecil dibandingkan gic (fuji ix). kata kunci: glass ionomer cement (gic), silika, perlekatan, scanning electron microscope (sem).? abstract name : dwi septiani study program : dentist education faculty : dentistry tittle : description attachment of silica 5% modified glass ionomer cement from sea sand with teeth by using scanning electron microscope (sem) glass ionomer cement (gic) is the most commonly used restoration material because of biocompatible material. gic is restoration material that can be attached to email and dentin physical chemically. the adhesion properties of teeth to restoration have an effect on marginal adaptation. this causes different attachment values. an alternative difference in attachment is needed by adding bioactive glass silica material to glass ionomer cement. in this study, silica was synthesized from sea sand by using kopresipitation method. this study aimed to obtain information about attachment of silica 5% modified glass ionomer cement from sea sand as mean value of distance between email and dentin surface with restoration by using scanning electron microscope (sem). samples were 4 maxillary premolars were classified into two groups which were applied gic (fuji ix) (n=2) and silica 5% modified gic as restorations (n=2). the specimens were immersed in 5% methylene blue solution for 24 hours, then were observed under sem. the study specimens were observed the mean distance of the attachment of the restoration material with the teeth (email and dentin). analysis descriptive statistics result showed mean value of distance between gic (fuji ix) with email and dentin surface were 11.74 4.642 m and 13.52 7.891 m while on silica 5% modified gic with email and dentin were 6.31 1.086 m and 9.33 2.361 m. conclusion of this study, there were a difference mean value of distance between silica 5% modified gic with email and dentin had smaller distance, as compared to gic (fuji ix). keywords : glass ionomer cement (gic), restoration material, silica,

Pengarang tidak dapat memberikan Full Text secara langsung, untuk mendapatkan full text silahkan menghubungi email pengarang : dwiseptiani839@gmail.com atau dapat mengisi Form LSS di bawah.

Literature Searching Service



Tulisan yang relevan

GAMBARAN KETEBALAN BIOFILM PADA GLASS IONOMER CEMENT (GIC) TIPE II MODIFIKASI PENAMBAHAN SILIKA DARI SINTESIS PASIR PANTAI (REZA UMAMI, 2019) ,

GAMBARAN KETEBALAN BIOFILM PADA GLASS IONOMER CEMENT MODIFIKASI HIDROKSIAPATIT 5% DARI SINTESIS CANGKANG KERANG DARAH (ANADARA GRANOSA) (Rani Milda Yanti, 2019) ,

GAMBARAN PENGGUNAAN BAHAN AMALGAM, RESIN KOMPOSIT DAN GLASS IONOMER CEMENT (GIC) DI RUMAH SAKIT GIGI DAN MULUT UNSYIAH PADA BULAN JULI DESEMBER 2014 (Nur Shabrina, 2016) ,


Kembali ke halaman sebelumnya


Pencarian

Advance



Jenis Akses


Tahun Terbit

   

Program Studi